Enhancing Adhesion of Si-Doped Diamond-like Carbon Coatings on Carbon Steel via Laser Cladding

A duplex coating system, consisting of a laser-cladded Fe-Cr-based interlayer and a silicon-doped diamond-like carbon (Si-DLC) top layer, was deposited on medium carbon steel substrate using laser cladding (LC) followed by plasma-enhanced chemical vapor deposition (PECVD). The LC interlayer (thickness of 1.5 mm, hardness of 455–620 HV0.3) was applied on both argon ion-etched and non-etched substrate surfaces. The microstructure and adhesion strength of the coatings were systematically investigated. The results show that the LC interlayer significantly enhanced the mechanical support for the Si-DLC coating, increasing adhesion strength by 4~5 times compared to direct deposition. Argon ion etching introduced micro-roughened surface features, increasing interfacial contact area and further boosting adhesion. A synergistic effect was observed between substrate hardness and ion etching in enhancing Si-DLC coating adhesion.