Enhanced Oxygen Evolution Reaction Catalytic Properties of Novel Nanowire Structures from FeCo‐MOFs/GO via Low‐Temperature Annealing

This is the authors' abstract. We don't add key points for this paper.

Metal‐organic frameworks (MOFs) often suffer from poor stability, making them suitable precursors for metal oxides/porous carbon catalysts in the oxygen evolution reaction via pyrolysis. High‐temperature treatment, however, leads to significant loss of active sites. To address this, Fe‐MOFs, FeCo‐MOFs, and FeCo‐MOFs/graphene oxide (GO) composites using a one‐pot hydrothermal method are synthesized and annealed at a low temperature of 300 °C. Characterization reveals that FeCo‐MOFs/GO composites possess unique nanowire structures mixed with a small amount of nanoflakes. It is believed that introducing graphene oxide plays a critical role in forming this structure, because the defects in GO provide numerous nucleation sites for nanowire growth. With high specific surface area and good stability, these nanostructures show a low overpotential of 261.5 mV at a current density of 10 mA cm − 2 and a Tafel slope of 20.47 mV dec −1 in 1 mol L −1 KOH alkaline water electrolysis. Density functional theory calculations further indicate that the synergistic effect of Fe and Co atoms enhances the catalytic activity.