Anion Substitution to Suppress the Voltage Hysteresis of Na3MnTi(PO4)3 as a Cathode Material for Sodium-Ion Batteries

The Mn-based polyanion compound Na3MnTi(PO4)3 (NMTP) with a Na superionic conductor (NASICON) structure has attracted incremental attention as a potential cathode material for sodium-ion batteries. However, the occupation of Mn2+ on Na+ vacancies usually leads to severe voltage hysteresis, which in turn results in significant capacity loss, slow Na+ diffusion kinetics, and poor cycling stability. Herein, anion-substituted compounds Na3MnTi(PO4)3-x(SiO4)x (x = 0.1, 0.2, and 0.3) are synthesized. It reveals that the SiO44- substitution could induce partial oxidation of Mn2+ to Mn3+, and the latter has a lower occupancy preference on Na+ vacancies. By the proposed charge compensation strategy, the Mn2+ occupation on Na+ vacancies can be significantly suppressed. As a result, the voltage hysteresis is substantially inhibited, and greatly improved electrochemical performance is achieved. This study offers an alternative strategy to address the voltage hysteresis associated with NMTP and other Mn-based NASICON cathode materials.