Nuclear reactor radiation and temperature effects on piezoelectric surface acoustic wave devices

Surface acoustic wave (SAW) resonators were characterized in-situ in a nuclear reactor environment at high-temperature. Devices based on lithium niobate (LiNbO3), aluminum nitride (sc-AlN), and thin-film aluminum nitride on sapphire substrate (AlN/sapphire) were tested up to 400 °C temperature and 1.9×1012 n/cm2s neutron flux. Shifts in device resonant frequency were detected in response to temperature and neutron flux. Devices undergo a frequency change when exposed to neutron flux. At 300 °C, AlN/sapphire produced the strongest neutron flux response about 1.02 ppm at 1.27×1012 n/cm2s neutron flux (5.7 × 104 rad-Si/hr neutron dose rate), compared to 0.30 ppm for LiNbO3 and 0.17 ppm for sc-AlN. While the transient kinetics in response to step change in neutron flux support the defect-accumulation mechanism, the concurrent measurement of device temperature using resistive temperature sensor suggests additional heating caused by absorption of gamma rays can also play a role. These results make SAW devices attractive candidates for sensor applications in extreme environments.