Electrochemical testing demonstrates reduced pitting corrosion in cast GCr15 bearing steel, indicating inoculation delays degradation by refining grain structures.
The corrosion resistance of bearing materials is crucial for the long-term service and high precision of modern equipment, and has aroused widespread research interest. Inoculation treatment is beneficial for improving the mechanical properties of GCr15 bearing steel, but its impact on corrosion behavior remains to be investigated. In the present work, the influence of inoculation treatment on the corrosion morphology, open circuit potential, impedance spectrum, and polarization curve evolution of GCr15 steel was studied through in situ corrosion morphology analysis and electrochemical testing. The results showed that the samples treated after inoculation showed a reduced tendency for pitting corrosion and an obviously improved corrosion resistance. This improvement is related to the transformation of columnar grains into equiaxed grains during the inoculation process, which reduces the amount and distribution of inclusions and pores, thereby delaying the rapid development of pitting corrosion. This study provides new insights into the corrosion mechanism of gestational steel.
No takes yet. Share an insight, caveat, or question.
Liu et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: