Effect Of Air-Abrasion And Er:Yag Laser On The Bond Strength Between The Metal Housing Of An Overdenture Attachment System And The Hard Relining Material

This is the authors' abstract. We don't add key points for this paper.

Objective. This study investigated the effect of air-abrasion and erbium:yttrium-aluminum-garnet (Er:YAG) laser treatments on push-out bond strength (PBS) between hard relining material and metal housing of an overdenture attachment system. Material and Methods. A total of 36 metal housings were randomly divided into 3 subgroups according to surface pretreatments (n=12): Control (no surface treatment; C), air-abrasion (A), and Er:YAG laser (L). Surface roughness (Ra) of specimens was determined using a profilometer. One additional specimen per group was evaluated by scanning electron microscopy (SEM). The hard relining material was bonded to metal housings, and a PBS test was performed using a universal testing machine. Data were statistically analyzed using 1-way analysis of variance (ANOVA), Tukey’s honestly significant difference (HSD), and Tamhane’s T2 tests (α=.05). Results. C and L groups showed the lowest and highest Ra values, respectively. The mean Ra of the A group was statistically different from the mean values of the C and L groups (P<.001). The L group showed higher PBS values than the C group (P<.05), whereas the A group exhibited statistically similar PBS values to both C and L groups (P>.05). Conclusions. Air-abrasion did not significantly increase the bond strength between the metal housing and hard relining material. Er:YAG laser irradiation noticeably improved the PBS but caused surface microcracks.