Ion Release and Apatite Formation of Resin Based Pit and Fissure Sealants Containing 45S5 Bioactive Glass

The purpose of this study was to evaluate a resin based pit and fissure sealant containing 45S5 bioactive glass (BAG) by examining its ion release, pH variation, and apatite-forming properties. To prepare the experimental materials, 45S5 BAG, used as a filler, was incorporated into the light curable resin matrix at concentrations of 0 (control), 12.5, 37.5, and 50.0 wt.%. Ion release, pH variation, and apatite formation (Raman spectrometer and scanning electron microscopy-energy-dispersive X-ray spectrometry measurements) were performed. While no ions were released from the control group, the experimental groups containing 45S5 BAG showed an increased release of Ca and P ions with increasing amounts of 45S5 BAG (p < 0.05). The pH of the experimental group remained high and was significantly different from the control group (p < 0.05). Unlike the control group, it was confirmed that the apatite peak was formed in the 50.0 wt.% BAG group for 90 days, and the apatite layer consisting of Ca and P was deposited on the surface. Thus, a resin based pit and fissure sealant containing 45S5 BAG is a promising material for preventing secondary caries by releasing ions and forming apatite.