Enhanced acetaminophen photodegradation under UV using anatase–rutile TiO2 phase heterojunction – Z-scheme mechanism and factors affecting efficiency

In this work, the commercial Hombikat UV-100 anatase (AH) was calcined at 1000 °C for 4 h to obtain a rutile phase grown on anatase (AR), proven by X-ray diffraction pattern. The dry powder of AH and AR were physically mixed to form AH + AR samples in different ratios. Although the characterization of AR revealed that it had microstructure bigger than AH, lower surface area, lower water-molecule absorption, higher surface states and lower charge separation, all mixed AH + AR samples, which had physically-induced tuning in phase heterojunction, outperformed the commercial TiO2 P25 in acetaminophen (ATM) photodegradation efficiency. This could be due to effective charge separation and more active sites involved as seen in the Z-scheme mechanism depicted based on their band-edge positions obtained from Mott-Schottky analysis, scavenger tests and ATM photodegradation efficiency. In addition, this work also showed that band-edge positions, band-gap energy and heterojunction were correlated in determining the ATM photodegradation efficiency.