Theoretical Studies on the Chemical Degradation and Proton Dissociation Property of PBI used in High-Temperature Polymer Electrolyte Membrane Fuel Cells

High-temperature polymer electrolyte membrane fuel cells (HT-PEMFCs) are gaining more and more attention due to their higher efficiency than low-temperature ones. Polybenzimidazole (PBI) membranes are the most popular membranes used in HT-PEMFCs. However, their chemical stability and chemical degradation mechanisms, which directly affect the lifetime of fuel cells, have been hardly reported. We applied the density functional theory and used ABPBI as an example membrane to investigate the chemical degradation mechanisms of PBI membranes. The possible degradation mechanisms that occurred on eight sites have been proposed, where sites 2 and 3 located on the phenyl ring are determined as two weak sites toward OH radical and oxygen molecule attack. When the terminal is the H atom at site 7, it is also weak under OH radical attack. Regarding these, the substituent effect on the chemical stability of polymers has been studied. By introducing four -C