Producing an antibacterial acrylic polyurethane coating with acylated mimosa tannins

This work aims to fabricate the antibacterial coating with green biocide successfully. For this purpose, mimosa tannins were acylated with lauroyl chloride’s aid and pyridine’s support as a catalyst in the 1,4-dioxane, hexane and xylene solvents. Infrared analysis showed that mimosa tannins synthesized in the 1,4-dioxane were acylated better than in the other two solvents. FE-SEM analysis of the paint film showed that the acylated mimosa tannins at a content of 5 % dispersed quite well in the polymer matrix. The results of analyzing the mechanical properties of the paint film containing acylated mimosa tannins with contents ≤5 % show that the mechanical properties of the paint film are only slightly reduced compared to the mechanical properties of the pure coating, reaching the values: adhesion of size #1; abrasion resistance of 132.8 L/mil; impact strength of 170 kg cm and a relative hardness of 0.78. Antibacterial testing shows that the paint film containing 5 wt% acylated mimosa tannins have good antibacterial activity.