The investigation of the energy harvesting performance using electrospun PTFE/PVDF based on a triboelectric assembly

This work presents an investigation into the energy harvesting performance of a combination of polytetrafluoroethylene (PTFE) and polyvinylidene fluoride (PVDF) materials prepared using a one-step electrospinning technique. Before electrospinning, different percentages of the 1 micron PTFE powder were added to a PVDF precursor. The surface morphology of the electrospun PTFE/PVDF fibre was investigated using a scanning electron microscope and tunnelling electron microscope. The structure was investigated using Fourier-transform infrared spectroscopy and x-ray diffraction analysis (XRD). A highly porous structure was observed with a mix of the α - and β -phase PVDF. The amount of β -phase was found to reduce when increasing the percentage of PTFE. The maximum amount of PTFE that could be added and still be successfully electrospun was 20%. This percentage showed the highest energy harvesting performance of the different PTFE/PVDF combinations. Electrospun fibres with different percentages of PTFE were deployed in a triboelectric energy harvester operating in the contact separation mode and the open circuit voltage and short circuit current were obtained at frequencies of 4–9 Hz. The 20% PTFE fibre showed 4 (51–202 V) and 7 times (1.3–9.04 µ A) the voltage and current output respectively when compared with the 100% PVDF fibre. The V oc and I sc were measured for different load resistances from 1 kΩ to 6 GΩ and achieved a maximum power density of 348.5 mW m −2 with a 10 MΩ resistance. The energy stored in capacitors 0.1, 0.47, 1, and 10 µ F from a book shaped PTFE/PVDF energy harvester were 1.0, 16.7, 41.2 and 136.8 µ J, respectively. The electrospun fibre is compatible with wearable and e-textile applications as it is breathable and flexible. The electrospun PTFE/PVDF was assembled into shoe insoles to demonstrate energy harvesting performance in a practical application.