Non‐isocyanate polyurethane‐acrylate as UV‐ and thermo‐responsive plasticizer for thermoplastic elastomer

A UV‐ and thermo‐responsive polyurethane‐acrylate prepolymer was synthesized from palm olein (PO o ) via a non‐isocyanate route. The process included epoxidation of PO o , carbonation of epoxidized palm olein (EPO o ) into polycyclic carbonate in a solvent‐free and mild condition (100°C, 1 atm), followed by reacting with ethylene diamine and acrylic acid. The chemical structure of the non‐isocyanate polyurethane‐acrylate (NIPUA) prepolymer was elucidated by 1 H and 13 C nuclear magnetic resonance (NMR) and Fourier transform‐infrared spectroscopy (FTIR), while weight average molecular weight of NIPUA was determined by gel permeation chromatography (GPC). The NIPUA (0–20 wt%) was incorporated with thermoplastic elastomer (TPE) as a plasticizer and cured under UV light and thermal stimulations. The cured NIPUA/TPE films were characterized by FTIR, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and tensile strength test. Under UV and thermal stimulations, the NIPUA/TPE demonstrated enhanced tensile properties (elongation at break >1280%, Young's modulus ~25 MPa), thermal properties (lower T g ), lower water contact angle, and shortened curing time as compared with the blank TPE. The 20 wt% NIPUA/TPE films exhibited susceptibility to enzymatic biodegradation and noncytotoxic to HEK 293 cells in vitro, demonstrated it's potential as a UV‐ and thermo‐responsive plasticizer for TPE in manufacturing of medical devices.