The development of low-temperature lithium metal batteries (LMBs) encounters significant challenges because of severe dendritic lithium growth during the charging/discharging processes. To date, the precise origin of lithium dendrite formation still remains elusive due to the intricate interplay between the highly reactive lithium metal anode and organic electrolytes. Herein, we unveil the critical role of interfacial defluorination kinetics of localized high-concentration electrolytes (LHCEs) in regulating lithium dendrite formation, thereby determining the performance of low-temperature LMBs. We investigate the impact of solvation structures of LHCEs on low-temperature LMBs by employing tetrahydrofuran (THF) and 2-methyltetrahydrofuran (2-MeTHF) as comparative solvents. The combination of comprehensive characterizations and theoretical simulations reveals that the THF-based LHCE featured with a strong solvation strength exhibits fast interfacial defluorination reaction kinetics, thus leading to the formation of an amorphous and inorganic-rich solid–electrolyte interphase (SEI) that can effectively suppress the growth of lithium dendrites. As a result, the highly reversible Li metal anode achieves an exceptional Coulombic efficiency (CE) of up to ∼99.63% at a low temperature of −30 °C, thereby enabling stable cycling of low-temperature LMB full cells. These findings underscore the crucial role of electrolyte interfacial reaction kinetics in shaping SEI formation and provide valuable insights into the fundamental understanding of electrolyte chemistry in LMBs.
Li et al. (Thu,) studied this question.