Response Surface Methodology Optimization of Resistance Welding Process for Unidirectional Carbon Fiber/PPS Composites

The use of thermoplastic composites (TPCs) as one of the lightweight solutions will inevitably encounter problems in connection. Resistance welding has the characteristics of high strength, simplicity, and high reliability, and is considered a very potential hot-melt connection technology. The resistance welding technology of unidirectional carbon fiber-reinforced polyphenylene sulfide composites (UCF/PPS) was systematically studied. The experimental results show that the 100-mesh brass mesh has the best resin wetting effect and heating efficiency, and the PPS/oxidized 100-mesh brass mesh composite resistance element (Ox-RE/PPS) has the highest welding strength. The welding failure mode changes from interface failure and RE failure to interlayer structure damage and fiber fracture. The single-factor experimental results show that the maximum welding strength is reached at 310 °C, 1.15 MPa, and 120 kW/m