Microstructure Evolution of Alloy 800H during Cold Rolling and Subsequent Annealing

The microstructure evolution during the cold rolling and subsequent annealing of Alloy 800H was investigated. Two distinct rolling methods, unidirectional rolling and cross-rolling, were intro-duced. Results show that better ductility was observed in the unidirectional rolling than in cross-rolling, whilst a higher volume fraction of large deformed grains was observed in the cross-rolled plates than in the unidirectionally rolled plates. Recrystallization occurred faster in plates from unidirectional rolling than from cross-rolling.