The phase composition of the pre-oxidized film on an alloy surface usually has a great influence on its corrosion resistance. In this work, the surface oxide film growth behavior in low-oxygen atmosphere at 720 °C of two 12Cr heat-resistant steels with different Mn content was studied, and their corrosion resistance in liquid lead–bismuth eutectic (LBE) with saturated oxygen at 600 °C was tested. The results indicated that the pre-oxidized film of 1.6Mn steel is mainly composed of large-size Mn–Cr spinel and Fe–Cr spinel, while that of improved 0Mn steel is mainly composed of continuous and dense Cr2O3 and Fe–Cr spinel. This is because Mn has a high diffusion rate in Cr2O3, so it can pass through the Cr2O3 layer and combine with O to form Mn-rich oxides, and then the Mn-rich oxides react with Cr2O3 to form Mn–Cr spinel. However, due to the high solubility of Mn in LBE, the Mn-rich pre-oxidized film of 1.6Mn steel will dissolve and fail quickly, so its long-term corrosion resistance in LBE is lower than that of 0Mn steel.
No takes yet. Share an insight, caveat, or question.
Cao et al. (2024) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: