Structural, thermal, surface, and electrical properties of Bi2O3 ceramics co–doped with Er–Ho–Tb rare earths

Face–centered cubic–Bi 2 O 3 (δ–phase) material is a better ion conductor when compared to other types of solid electrolytes that have been declared in the literature due to its anion–defective crystal configuration, and hence it can be a promising solid electrolyte choice for intermediate temperature SOFC applications. In this research, Er–Ho–Tb co–doped Bi 2 O 3 compounds were successfully synthesized by the solid–state reaction method and characterized using the XRD, TG & DTA, FPPT, and FE–SEM techniques. Apart from sample 4Er4Ho4Tb, each sample became stable with a cubic δ–phase at room temperature, according to XRD patterns. The DTA curves revealed no exothermic or endothermic peaks, implying a phase change in the constant heating cycle. The conductivity of Ho–rich compositions was higher than that of others, confirming the impact of cation polarizability on conductivity. In addition, at 700 °C, the sample 4Er8Ho4Tb with 1:2:1 content ratios had the highest conductivity of 0.29 S/cm. The porosity on the grain boundaries increased with doping, leading to higher grain boundary resistance, which could be responsible for the conductivity drop.