Low carbon, low cost and sustainability are important development trends of ultra-high-performance concrete (UHPC). In this study, municipal solid waste incineration bottom ash (MSWIBA) was used to replace 5%, 10%, 20% and 30% of quartz sand (QS), respectively, and the effect of the MSWIBA substitution rate on the workability, wet packing density, mechanical properties, shrinkage, resistance to chloride ion corrosion, and resistance to sulfate corrosion of UHPC was studied. The mechanism analysis was carried out by combining X-ray diffraction (XRD), thermogravimetric analysis (TG), and scanning electron microscopy (SEM) tests, and UHPC heavy metal leaching tests, environmental impact assessment, and economic analysis were conducted. Results show that the active silicon and aluminum components in MSWIBA reacted with cement hydration products to optimize the matrix density. MSWIBA has an internal curing effect, which is beneficial for reducing the shrinkage of UHPC. When the MSWIBA replacement rate is 10%, the 28-day compressive strength of MSWIBA-UHPC is 128.7 MPa, which is equivalent to the benchmark group. The fluidity, corrosion resistance and heavy metal leaching all meet the requirements. The energy consumption, carbon emissions and costs are reduced by 0.22%, 2.30% and 6.67%, respectively. The research results can provide a reference for the development of ecological UHPC with economic, low-carbon and environmental benefits, as well as the harmless disposal and resource utilization of hazardous wastes such as MSWIBA.
Liu et al. (Sat,) studied this question.