Chinese lacquer (urushi), a traditional East Asian coating material, has been used for more than 7000 years due to its durability, gloss, and cultural significance. However, its long-term stability under natural light remains insufficiently studied, especially regarding the role of mineral pigments in modulating photoaging behavior. In this study, three traditional lacquer coatings pigmented with cinnabar (HgS), orpiment (As2S3), and lapis lazuli were subjected to natural light aging for nine weeks. Colorimetric analysis revealed rapid chromatic changes during the initial stage of exposure, followed by slower transformations, with cinnabar-based red lacquer showing superior stability compared to orpiment- and lapis-based coatings. Gloss measurements and surface roughness analyses demonstrated a strong negative correlation, with yellow lacquer exhibiting the most severe gloss loss (≈30%) and roughness increase (≈89%), consistent with scanning electron microscopy observations of microcracking and surface deterioration. Fourier-transform infrared spectroscopy (FTIR) indicated pigment-dependent oxidative degradation, characterized by intensified carbonyl and aromatic C=C bands. Collectively, the results confirm that mineral pigments strongly influence the optical, chemical, and structural stability of lacquer coatings. From a conservation perspective, cinnabar-based lacquers exhibit higher resilience, whereas orpiment- and lapis-colored coatings are highly vulnerable, underscoring the need for pigment-specific preservation strategies for lacquerware cultural heritage.
Liu et al. (2025) studied this question.