Fabrication and Parameter Optimization of High-Melting-Point Pure Cr by Binder Jetting Additive Manufacturing

BJ3DP has unique advantages compared to other energy-beam-based additive manufacturing technologies, such as lower residual stress, arising from the lack of heat during the printing process and the uniformity of the sintering process. However, attaining both high density and dimensional precision in metallic materials remains a challenge in BJ3DP. This study presents a systematic investigation into the fabrication of high-melting-point pure chromium (Cr) via binder jetting 3D printing (BJ3DP), with a focus on optimizing the printing parameters and sintering conditions. An orthogonal experiment identified the optimal printing parameters as a layer thickness of 75 μm and a binder saturation of 60%, which resulted in green parts with a relative density of 57.1%—a representative value for BJ3DP processes that demonstrates effective parameter optimization. Subsequently, the green parts were sintered at 1800 °C for 9 h, resulting in a maximum density of 97.35%. The hardness of the as-sintered BJ3DP Cr parts was superior to that of samples produced by conventional levitation melting (184.20 HV vs. 171.20 HV). This work demonstrates that the no-heat printing strategy of BJ3DP effectively mitigates issues related to residual stress and cracking, providing a viable method for producing high-melting-point metallic materials.