Fluoro-Functionalized Silsesquioxane Polymer-Based High Hydrophobic Coatings for Enhancing Properties of Kraft Paper

Paper plays an important role in the packaging industry due to its low cost, light weight, recyclability and biodegradability. However, the use of paper as a packaging material is severely limited due to its hydrophilicity caused by the hydroxyl groups of cellulose. This study reports a simple preparation of highly hydrophobic kraft paper by a one-step dip coating method using [3-(2,2,3,3-tetrafluoropropoxy)propyl]silsesquioxane, {3-[(2,2,3,3,4,4,5,5-octafluoropentyl)oxy]propyl}silsesquioxane or {3-[(2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoroheptyl)oxy]propyl}silsesquioxane as hydrophobic agents. As a result of modification of kraft paper, a stable covalently bonded coating is formed on its surface. The coated kraft paper has demonstrated (1) high water resistance (the water contact angle (WCA) values were 124–141°, and the water absorption and the water vapor permeability (WVP) rates were significantly decreased), (2) excellent resistance to aggressive environments and temperature, (3) enhanced mechanical properties (tensile strength increased from 46.8 to 70.8 MPa), and (4) high wear resistance, as confirmed by sandpaper abrasion, bending, and finger-wipe tests. It was shown that the maximum contact angle values were achieved for kraft paper modified with a 5% polymer solution. The results of this study have great potential, given the simplicity of the modification method, for use in the production of paper-based packaging materials with water-repellent, enhanced mechanical and moisture-protective properties.