Ni-Mo alloy coating has shown exciting potential as a candidate to replace chromium coating. In this paper, Ni-Mo alloy coatings were successfully electrodeposited from a citrate/ammonia bath, and the effect of the bath pH values over a wide range (4–10) on the characteristics and corrosion resistance of Ni-Mo alloy coating was studied in detail. Results show that all the deposited Ni-Mo alloy coatings consist of a crystalline solid-solution Ni(Mo) fcc structure. An increase in bath pH values could facilitate the deposition of Mo, thereby increasing the Mo content and decreasing the crystallite size of Ni-Mo alloy coatings. However, there are subtle gaps between the coarse grains on the surface of the Ni-Mo alloy coating deposited at pH 10. These subtle gaps tend to form between the coarse grains on the surface of the electrodeposited Ni-Mo alloy coating because of the relatively high Mo content, refined grains, and appropriate morphology. The Ni-Mo alloy coating deposited at pH 9 exhibits optimal corrosion resistance, attributed to its lowest corrosion current density icorr (7.31 × 10−6 A cm−2), the strongest polarization resistance (11.13 kΩ·cm−2), and impedance value, which are mainly contributed to by the coating resistance and charge-transfer resistance.
Shi et al. (Sun,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: