The reliable joining of dissimilar stainless steel and carbon steel remains a critical challenge in Metal Inert Gas (MIG) welding due to complex thermal–metallurgical interactions and the formation of brittle phases at the weld interface. In this study, a Taguchi-based design of experiments was employed to systematically optimize MIG welding parameters for SUS201/S20C dissimilar joints using a SUS201 filler wire, with particular attention to the welding current, voltage, travel speed, and electrode stick-out. The welding process was performed using an automatic welding robot. Tensile specimens were tested on a universal testing machine. Microstructural analysis was performed using a metallurgical microscope. The microstructure reveals that the development of the carbon side’s large ferrite and the stainless steel side’s δ-ferrite both significantly degrade joint quality. Among all process parameters, electrode stick-out is identified as the most influential parameter governing both tensile and bending performance, highlighting a critical process sensitivity that has received limited attention in prior studies. Optimized parameter combinations are required to maximize tensile and flexural responses. The highest tensile strength is 450.96 MPa. These findings advance the understanding of parameter–microstructure–property relationships in dissimilar MIG welding. Future work applying numerical welding simulations and advanced evaluation techniques is recommended.
Thien et al. (Sun,) studied this question.