Electrochemical Sensor Based on a Fe3O4 and Graphene Composite for the Detection of Myristicin

This study aims to develop an electrochemical sensor based on a glassy carbon electrode (GCE) modified with Fe3O4 and graphene for the detection of myristicin as a characteristic compound in nutmeg plants. Electrode modification materials were prepared from a combination of graphene and magnetite, synthesized via a hydrothermal method, and further characterized using X-ray diffraction (XRD), scanning electron microscope–energy dispersive spectroscopy (SEM-EDS), and transmission electron microscopy (TEM). The two modifying materials were then optimized, and the optimum conditions were obtained at a w/w ratio of 1:2, which was applied to the GCE surface using the drop-casting technique. The electrochemical performance of the Fe3O4/graphene-modified electrode was evaluated under optimum experimental conditions using a Britton–Robinson buffer solution at pH 5. The scan-rate analysis of the electrode to evaluate its electrochemical performance showed an increase in surface area from 0.101 cm2 for the bare GCE to 0.534 cm2 for the GCE/Fe3O4–graphene. Electroanalytical performance was evaluated using differential pulse voltammetry (DPV), which showed a linear response over the concentration range of 1–100 µM, with a limit of detection of 0.19 µM and a limit of quantitation of 0.58 µM. The developed electrode was applied successfully to detect myristicin in nutmeg seed extract samples, and its calculated concentrations were not significantly different from those obtained with the GC-MS method. These results suggest that the developed sensor may have further potential as an alternative detection tool for characterizing electroactive compounds in nutmeg plants.