Refractory high-entropy alloys (RHEAs) have garnered attention for their exceptional high-temperature mechanical properties, making them suitable for aerospace and energy applications. However, balancing strength and ductility remains a challenge due to the presence of Laves phases. In this study, Al0.5Nb0.5TiV2Zrx (x = 0–2.0) alloys were prepared using vacuum arc melting, and their microstructural evolution and mechanical properties were analyzed. At room temperature, the Al0.5Nb0.5TiV2Zr0.5 alloy exhibits the highest yield strength (1658.1 MPa), which is primarily attributed to strong lattice distortion induced by Zr and moderate precipitation strengthening from Laves phases. In contrast, at higher Zr contents, excessive Laves phase precipitation promotes stress concentration, leading to a marked reduction in both strength and ductility. High-temperature compression tests revealed that the Al0.5Nb0.5TiV2Zr0.5 and Al0.5Nb0.5TiV2Zr1.5 alloys still exhibited over 50% compressive plasticity at 800 °C and 1000 °C. However, when the temperature reached 1000 °C, the instability of the Laves phase led to a reduction in the yield strength to below 160 MPa, indicating that the effect of solid-solution strengthening was no longer significant under high-temperature conditions. These findings clarify the critical role of Zr content and temperature in governing the microstructural and mechanical evolution of the Al–Nb–Ti–V–Zr system and provide a theoretical basis for achieving an optimized strength–ductility balance in RHEAs through compositional control.
Zhao et al. (2026) studied this question.