Site-selective enhancement of Eu emission in delta-doped GaN

Europium-doped gallium nitride (GaN:Eu) is a promising platform for classical and quantum optoelectronic applications. When grown using organometallic vapor-phase epitaxy, the dominant red emission from Eu exhibits an inhomogeneous photoluminescence (PL) spectrum due to contributions from several nonequivalent incorporation sites that can be distinguished with combined excitation-emission spectroscopy. Energy transfer from the GaN bandgap to the majority site is inefficient, limiting the performance of GaN:Eu light-emitting diodes (LEDs) and resulting in an inhomogeneous emission spectrum dominated by disproportionate contributions from minority sites. In this work, we use site-selective spectroscopy to characterize the photoluminescence properties of delta-doped structures with alternating doped and undoped layers of varying thicknesses and demonstrate that they selectively enhance emission from the majority site when compared to uniformly doped samples. Samples with 2- and 10-nm doped layers show much greater PL intensity per Eu concentration as well as more efficient energy transfer to the majority site, which are both highly desirable for creating power-efficient LEDs. Meanwhile, a sample with 1-nm doped layers shows emission only from the majority site, resulting in a narrow, homogeneous emission spectrum that is desirable for quantum technologies. This utilization of delta-doping has the potential to be broadly applicable for engineering desirable defect properties in rare-earth doped semiconductors.