The electronic energy loss spectra of ceria (CeO2) irradiated with swift heavy ions (27 MeV Xe and 946 MeV Au) in the electronic slowing down regime were measured for bulk sintered samples and nanoparticles by using a double Cs-corrected transmission electron microscope. The low-loss region as well as the core-loss region, including the oxygen K-edge and cerium M4, 5 white lines, were recorded. No strong lattice disorder was found in the low-loss peaks for both types of samples showing the same bulk oxygen plasmon loss peak at about 15 eV. However, there is a clear evidence of cerium reduction to the trivalent oxidation state after irradiation for the sintered samples as shown by the K-edge shape of oxygen and decrease of the Ce M4/M5 intensity ratio. A similar change of the M4/M5 intensity ratio was observed for the irradiated nanoparticles with respect to the virgin sample owing to the high energy input inside the nanograin. The effect of radiation damage on electron energy loss spectroscopy data is analyzed for both types of samples and irradiation conditions.
Costantini et al. (2026) studied this question.