Effect of cBN Addition on Phase Composition, Microstructure, Wear Resistance, and Corrosion Resistance of CoCuNiTi + x cBN (x = 0.0, 0.5, and 1.0 wt.%) High-Entropy Alloy Coatings

Although 45 steel is widely used in the manufacture of mechanical parts, its application in harsh working conditions is limited owing to its low hardness, poor wear resistance, and corrosion resistance. Laser cladding can enhance the performance of the working surface without sacrificing substrate toughness. CoCuNiTi HEACs with different cBN additions were successfully prepared on a 45-steel substrate. The phase structure, microstructure, elemental composition, wear, and corrosion behavior of CoCuNiTi + x cBN (x = 0.0, 0.5, and 1.0 wt.%) HEACs were investigated using XRD, OM, SEM, EDS, friction and wear tester, and electrochemical workstation, respectively. The results show that all three coatings exhibit a dual-phase structure composed of FCC and BCC phases. The addition of cBN transforms the alloy phase structure from the original FCC main phase to the BCC main phase. The incorporation of cBN significantly reduces the lattice constant and cell volume of the alloy phase. The change in the alloy phase density is negatively correlated with the cell volume. CoCuNiTi + x cBN (x = 0.0, 0.5, and 1.0 wt.%) alloys have a dendritic structure. No pores were observed in the cBN-containing sample. The content of Ti in the primary phase is the highest. Co is enriched in the dendrite region, and Cu is enriched in the interdendrite region. The significant reduction in the average segregation coefficient for cBN-containing samples is attributed to the heterogeneous nucleation of the alloy melt at lower undercooling levels and the significant increase in the diffusion rate. The friction coefficient of the alloy decreases significantly with increasing cBN content. The sample with 1.0 wt.% cBN shows the best wear resistance, mainly due to the combined effects of hard particle support, solid solution strengthening, phase interface reduction, and high thermal conductivity of cBN. The sample with 1.0 wt.% cBN has the largest capacitive arc radius and charge-transfer resistance, along with the lowest annual corrosion rate, indicating optimal corrosion resistance. This is primarily related to the reduction in pore defects caused by cBN addition, hindrance of uniform penetration of the corrosive medium by dispersed cBN particles, and increased complexity of the anodic dissolution process. CoCuNiTi HEACs reinforced by cBN can simultaneously improve the wear and corrosion resistance of the surface of the 45-steel substrate, providing a feasible strategy for the design of high-performance protective coatings.