Design, Processing, and Properties of WTaCrV-Hf Multi-principal Element Alloys

Refractory multi-principal element alloys are candidates for high-temperature structural components due, in part, to their high strength and high melting points. Single-phase materials are initially preferred for isotropic material properties as a function of time and temperature in service conditions. This work outlines a computational rank-ordering and experimental validation methodology for single-phase body-centered-cubic phase stability in WTaCrV-Hf alloys using order–disorder transition temperature. Eight compositions were fabricated by arc-melting and heat-treated at 1400 °C for 24 hrs. X-ray diffraction, energy-dispersive x-ray spectroscopy, and Vickers hardness testing showed alloys with order–disorder transition temperatures below 600 °C formed a single-phase body-centered-cubic structure during solidification and remained single-phase after heat-treatment. The sample possessing the lowest order–disorder transition temperature exhibited slip traces suggestive of room-temperature plastic deformation under Vickers indentation, with both heat-treated single-phase samples exhibiting hardnesses over 800 HV with little cracking compared to tungsten. These results establish order–disorder transition temperature as a viable predictive parameter for multi-principal element alloy phase stability. The methodology outlined in this work provides a framework for future design, fabrication, and characterization of high-temperature structural multi-principal element alloys.