The correlation between fouling-driven corrosion and magnetic Barkhausen noise (MBN) in AH36 naval steel was investigated under real Mediterranean seawater conditions over a 12-month immersion period. A custom-designed MBN analyzer was used to monitor four MBN parameters at monthly intervals: RMS amplitude (MBNRMS), peak amplitude (MBNpeak), peak field position (MBNpeak pos.), and full width at half maximum (MBNFWHM). Complementary characterization included pit morphology analysis, X-ray diffraction (XRD) of corrosion products, and quantitative biofouling community profiling. Three distinct MBN evolution regimes were identified, corresponding to active pitting (T0–T3), transitional oxide formation (T3–T6), and mature corrosion equilibrium (T6–T12). Over the full exposure period, MBNRMS decreased by 50.4% and MBNpeak pos. increased by 83.3%, consistent with domain wall pinning at pit stress concentrations and electromagnetic shielding by paramagnetic corrosion product layers (γ-FeOOH, β-FeOOH, α-FeOOH). Pearson correlation analysis revealed near-unity relationships between MBNRMS and maximum pit depth (r = −0.982, p < 0.01), supporting its potential use as a quantitative non-destructive indicator of corrosion severity under comparable exposure conditions. Biofouling, particularly sulfate-reducing bacteria (SRB)-dominated communities and biogenic iron sulfides (mackinawite, greigite), was identified as a statistically significant secondary correlate of MBN signal intensity (r = −0.944 vs. SRB fraction). A composite diagnostic threshold of (MBNRMS × MBNpeak)/MBNFWHM ≈ 0.015 effectively discriminated active pitting from passive rusting. These findings provide a physically grounded framework for multiparametric MBN analysis as a non-destructive condition monitoring tool, with the caveat that the reported correlations are descriptive and require independent validation before deployment in regulatory inspection protocols.
Vourna et al. (Sun,) studied this question.