Improved Analysis of Manganese in Steel Samples Using Collinear Long–Short Double Pulse Laser-Induced Breakdown Spectroscopy (LIBS)

A long-short double pulse laser-induced breakdown spectroscopy (long-short DP-LIBS) method was employed to improve the analytical performance of LIBS for the measurement of manganese in steel samples. The long pulse with a duration of 60 μs was generated using a neodymium-doped yttrium aluminum garnet (Nd:YAG) laser which was operated at free-running (FR) mode. To investigate the detection ability without sample preparation, the steel washers were tested using single-pulse LIBS (SP-LIBS) and long-short DP-LIBS, respectively. The measurement results show that long-short DP-LIBS was able to record clear spectra from the steel washers with a surface layer. Through the observation on the laser craters with a scanning electron microscope (SEM), the results suggest that the improvement in detection ability can be attributed to the pre-irradiation effect of long-pulse laser beam. Next, the analytical performance for quantitative measurement of manganese was evaluated employing ten standard steel samples. The results show that the linearity fit (R²) of the calibration curve is 0.988 for long-short DP-LIBS, whereas, R² is only 0.810 for SP-LIBS under the same measurement conditions. The repeated measurement results show that the average relative standard deviation (RSD) of the tested samples is 29.3% for SP-LIBS and is 10.5% for long-short DP-LIBS. The prediction results also show that the average relative error of prediction (REP) is 94.9% for SP-LIBS and is 4.9% for long-short DP-LIBS.