In the current work, several heat treatments were carried out below and above the beta-transition temperature of the Ti–6Al–4V alloy followed by aging at 550 °C for 6 hours. The resultant microstructures and their effects on the mechanical properties of Ti–6Al–4V alloy were investigated. The results showed that solution treatment of Ti–6Al–4V samples followed by water quenching from β and α/β fields raised the alloy hardness from 380 to 575 and 656 HV, respectively, while no remarkable changes were observed after aging. The hot tensile strength of the as-forged sample increased from 671 to 756 MPa after water quenching from the ß- or α/ß- field, while the air cooling from β-phase field decreased the tensile strength to 644 MPa. The fracture mode of the tensile samples was more ductile in case of the solution-treated samples compared to the as-forged samples. A subsurface layer was formed due to the diffusion of oxygen into the surface at high temperatures. This layer which is known as ‘oxygen diffusion layer’ masked the differences of wear behaviour of the specimens.
No takes yet. Share an insight, caveat, or question.
El‐Hadad et al. (2017) studied this question.