Sluggish and narrow process window of phthalonitrile resin has tremendously limited their wide applications. In this work, a novel phthalonitrile containing benzoxazine (4,4′‐(((propane‐2,2‐diylbis (2H‐benzo [e] [1,3]oxazine‐6,3 (4H)‐diyl) bis(3,1‐phenylene))bis(oxy)) diphthalonitrile, BA‐ph) with ortho‐diallyl bisphenol A (DABPA) was investigated. The processing window of the BA‐ph/DABPA blends were found from 50°C to 185°C, which was significantly broader than that of the pure BA‐ph (120–200°C). The composites were prepared through a curing process involving sequential polymerization of allyl moieties, ring‐opening polymerization of oxazine rings and ring‐forming polymerization of nitrile groups. BA‐ph/DABPA/GF(glass fiber) composite laminates were prepared in this study, and the composite laminate with BA‐ph/DABPA molar ratio of 2/2 showed an outstanding flexural strength and modulus of 560 MPa and 37 GPa, respectively, as well as a superior thermal and thermo‐oxidative stability up to 408 and 410°C. These outstanding properties suggest that the BA‐ph/DABPA/GF composites are suitable candidates as matrices for high performance composites. POLYM. ENG. SCI., 56:150–157, 2016.
No takes yet. Share an insight, caveat, or question.
Luo et al. (2015) studied this question.