Copper functions as an exceptionally efficient conductor, garnering considerable interest in electrical and thermal applications; however, its relatively malleable nature and insufficient durability may hinder its structural effectiveness. This study focused on the development of copper-based nanocomposites by reinforcing a copper matrix with co-precipitated CuO/Al2O3 nanoparticles (varying from 0 to 10 wt% in increments of 2%). A thorough examination was conducted regarding the microstructural characteristics, mechanical properties, and the electrical and thermal conductivities of the composites. X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDS) analysis validated the successful synthesis of nano-sized CuO and Al2O3 phases, with an estimated crystallite size of 33.2 ± 2.4 nm. Scanning electron microscopy revealed a relatively uniform distribution of nano-oxides within the copper matrix, albeit with signs of particle agglomeration at higher loading levels. The durability of the copper exhibited a significant enhancement attributed to the nano-oxide reinforcement, achieving an 180% increase relative to pure copper with a 10% reinforcement addition. Consequently, the tensile strength increased by approximately 68% (from around 154 MPa to nearly 260 MPa), while maintaining an exceptional level of ductility. The electrical conductivity of copper remained largely unchanged with the addition of nanoparticles; rather, a slight improvement in conductivity and a ~30% rise in thermal conductivity were observed at the maximum reinforcement level. This research work presents a copper-based nanocomposite that offers remarkable potential for applications requiring enhanced strength, wear resistance, and exceptional electrical and thermal conductivity.
Ameh et al. (Thu,) studied this question.