Research on Fatigue Damage and Pitting Mechanism of Gears in Offshore Wind Power

In response to the problem that the gears for offshore wind power are prone to cyclic stress and pitting damage under specific conditions, a finite element analysis method was adopted to establish numerical models for the distribution of cyclic stress on the gears and the dynamic expansion of pitting. Based on the material properties of ASTM5140 alloy structural steel, simulations were conducted using ANSYS 2024 R1 for contact stress analysis during gear meshing and COMSOL 6.3 for the evolution of pitting in a corrosive environment over a 120-h period. The results showed significant stress concentration in the tooth root fillet area under cyclic loads, with a maximum equivalent contact stress of 2.838 × 108 Pa, which was identified as the key region for fatigue damage. Based on the simulated stress amplitude and material fatigue parameters, the predicted fatigue life of the gear under typical offshore operating conditions was approximately 13.3 years. In the corrosive environment, pitting pits exhibited an accelerating expansion trend, with pit volume increasing by approximately 125% and internal surface area by approximately 54% over 120 h. The volume growth followed a cubic polynomial, and the surface area growth followed a quadratic polynomial over time. These research results provide a quantitative basis for fatigue life assessment and corrosion protection design of offshore wind power gears.