Epitaxial GeSn Obtained by High Power Impulse Magnetron Sputtering and the Heterojunction with Embedded GeSn Nanocrystals for Shortwave Infrared Detection

GeSn alloys have the potential of extending the Si photonics functionality in shortwave infrared (SWIR) light emission and detection. Epitaxial GeSn layers were deposited on a relaxed Ge buffer on Si(100) wafer by using high power impulse magnetron sputtering (HiPI-MS). Detailed X-ray reciprocal space mapping and HRTEM investigations indicate higher crystalline quality of GeSn epitaxial layers deposited by Ge HiPI-MS compared to commonly used radio frequency magnetron sputtering (RF-MS). To obtain a rectifying heterostructure for SWIR light detection, a layer of GeSn nanocrystals (NCs) embedded in oxide was deposited on the epitaxial GeSn one. Embedded GeSn NCs are obtained by cosputtering deposition of (Ge1-xSnx)1-y(SiO₂)y layers and subsequent rapid thermal annealing at a low temperature of 400 °C. Intrinsic GeSn structural defects give p-type behavior, while the presence of oxygen leads to the n-character of the embedded GeSn NCs. Such an embedded NCs/epitaxial GeSn p-n heterostructure shows superior photoelectrical response up to 3 orders of magnitude increase in the 1.2-2.5 μm range, as compared to performances of diode based only on embedded NCs.