Dielectric studies of CuWO4 crystals

The dielectric constant, ϵ′, dielectric loss, tan δ, and the conductivity, σac, of as-grown, air and argon annealed single crystals and polycrystalline pellets of CuWO4 are measured in the frequency range 102 to 104 Hz and in the temperature range 37 to 477 °C. Initially ϵ′, increases slowly with temperature up to 327 °C, beyond which it rises exponentially. A. dielectric anomaly is also observed in the tan δ versus temperature curves. The values of activation energy for the conduction, calculated from ln σac versus 103/T data, are compared with the values of thermal activation energy, computed using dielectric constant versus temperature data. Im Temperaturbereich von 37 bis 477 °C werden Dielektrizitätskonstante ϵ′, Verlustwinkel tan δ und Leitfähigkeit σac von ursprünglich gezogenen sowie in Luft und Argon getemperten Einkristallen und polykristallinen Preßlingen von CuWO4 im Frequenzbereich von 102 bis 104 Hz gemessen. Anfänglich nimmt ϵ′ schwach zu mit der Temperatur bis zu 327 °C, darüberhinaus steigt es exponentiell. Eine dielektrische Anomalie wird auch für die tan δ-Temperatur-Kurven beobachtet. Die Werte der Aktivierungsenergie für die aus den ln σac-103/T-Kurven berechnete Leitfähigkeit werden mit den Werten der thermischen Aktivierungsenergie verglichen, die aus dem Verlauf der Dielektrizitätskonstante über der Temperatur berechnet werden.