Electrical and rheological percolation in poly(vinylidene fluoride)/multi‐walled carbon nanotube nanocomposites

Nanocomposites of poly(vinylidene fluoride) (PVDF) and multi‐walled carbon nanotubes (MWCNTs) were prepared through melt blending in a batch mixer (torque rheometer equipped with a mixing chamber). The morphology, rheological behavior and electrical conductivity were investigated through transmission electron microscopy, dynamic oscillatory rheometry and the two‐probe method. The nanocomposite with 0.5 wt% MWCNT content presented a uniform dispersion through the PVDF matrix, whereas that with 1 wt% started to present a percolated network. For the nanocomposites with 2 and 5 wt% MWCNTs the formation of this nanotube network was clearly evident. The electrical percolation threshold at room temperature found for this system was about 1.2 wt% MWCNTs. The rheological percolation threshold fitted from viscosity was about 1 wt%, while the threshold fitted from storage modulus was 0.9 wt%. Thus fewer nanotubes are needed to approach the rheological percolation threshold than the electrical percolation threshold.