Well-developed bipolar resistive switching behaviors have been revealed in Pt/GaOx/ITO stacks without an electroforming process. By substituting platinum with titanium as the top electrode, switching polarity changed from “counter-Figure-8” to “Figure-8.” The modulation of Schottky barrier at the Pt/GaOx interface induced by migration of oxygen vacancies was proposed to explain the switching in Pt/GaOx/ITO stacks, while the switching in Ti/GaOx/ITO stacks was ascribed to the redox reaction at the Ti/GaOx interface. Our experimental result further confirms the migration of oxygen vacancies in the vicinity of the electrode area plays an important role in the resistive switching process.