Doping of CdTe using CuCl₂ Solution for Highly Efficient Photovoltaic Devices

Here, we report doping of cadmium telluride (CdTe) thin film solar cells using copper (II) chloride (CuCl 2 ) solution in deionized water. The CdTe thin films were immersed in 0.1 mmol CuCl 2 solution in water and annealed in the temperature range of 180 - 240 °C for various time durations. The devices were completed using thermally evaporated gold (Au) and measured under simulated AM1.5G spectrum. The average device efficiency of CuCl 2 treated CdTe devices increased to 13.7 % (best cell reaching 14.0%) with significant improvement on open-circuit voltage (V OC ) as compared with 12.4% (best cell 12.7%) for thermally evaporated Cu doped CdTe devices. For CuCl 2 treated CdTe devices, we found higher photoluminescence (PL) intensity and longer carrier life time at room temperature indicating solution based doping offers better control of Cu doping density as compared with evaporated Cu.