The metastable phase Ni2Mo and the initial stages of ordering in NiMo alloys

The initial stages of ordering in Ni3Mo and Ni4Mo have been investigated by transmission electron microscopy and diffraction. The development of long-range order in Ni3Mo is associated with decomposition into the two metastable phases Ni2Mo and Ni4Mo, which are eventually replaced by the equilibrium Ni3Mo at a later stage of ordering. Evidence for the presence of metastable Ni2Mo phase was also found during the early stages of ordering of Ni4Mo. The presence of the metastable phase Ni2Mo at Ni4Mo composition and that of Ni2Mo and Ni4Mo at Ni3Mo composition can be explained in terms of the recent thermodynamic calculations of the ground states of ordered binary alloys by Cahn and his co-workers. Die Ausgangszustände der Ordnung in Ni3Mo und Ni4Mo wurden mit Transmissionselektronenmikroskopie und Beugung untersucht. Die Entwicklung von Fernordnung in Ni3Mo ist mit der Zerlegung in zwei metastabile Phasen Ni2Mo und Ni4Mo verbunden, die eventuell durch die Gleichgewichtsphase Ni3Mo in einem späteren Zustand der Ordnung ersetzt werden. Hinweise für die metastabile Ni2Mo-Phase wurden auch während der frühen Ordnungszustände von Ni4Mo gefunden. Die Anwesenheit der metastabilen Phase Ni2Mo bei der Ni4Mo-Zusammensetzung und die von Ni2Mo und Ni4Mo bei Ni3Mo-Zusammensetzung kann mit kürzlichen thermodynamischen Berechnungen der Grundzustände der geordneten binären Legierungen von Cahn und seinen Mitarbeitern erklärt werden.