We report a pressure-induced structural phase transformation in an additively manufactured (AM) AlCrFe2Ni2 high-entropy alloy. High laser scan-speed processing during AM has been shown to strongly suppress FCC formation, yielding BCC/B2-dominant microstructures. Synchrotron x-ray diffraction reveals a reversible BCC/B2 → HCP transition near ∼13 GPa that mirrors the α-Fe → ɛ-Fe transformation in elemental iron. Notably, this iron-like phase change occurs despite substantial chemical disorder and multi-element site occupancy, demonstrating that the BCC lattice instability leading to close-packed polymorphs can persist in a highly disordered matrix. At ambient pressure, AlCrFe2Ni2 exhibits robust ferromagnetic behavior associated with the BCC/B2 phase. The observation of an α-Fe–like polymorphic pathway in a chemically complex alloy shows that classic cubic-to-close-packed transformation physics is not extinguished by compositional complexity. As a result, AlCrFe2Ni2 emerges as a model system for exploring pressure-driven polymorphism and potential magneto-structural coupling in high-entropy alloys.
Sereika et al. (Wed,) studied this question.