Reversible Crystal Orientation Control in Conjugated Polymers for Field-Effect Transistors

The ability to tailor different crystal orientations (i.e., edge-on and face-on) in conjugated polymers remains essential for optimizing optoelectronic device performance and elucidating fundamental structure–property relationships. Despite significant progress in molecular engineering, the ability to achieve desirable conjugated polymer orientations and execute reversible transformations between them remains limited. This study designed a concerted strategy to reversibly tailor the crystal orientations in isoindigo-based donor–acceptor conjugated polymers (denoted as PII2T). This was achieved through sequential mechanical rubbing and solvent vapor annealing, which allowed for a direct correlation between the crystal orientation and carrier transport properties. Specifically, the edge-on orientation present in the as-cast PII2T film gradually transitioned to a predominant face-on orientation upon mechanical rubbing at elevated temperatures, accompanied by the formation of large-scale anisotropic crystal alignment along the rubbing direction. Subsequently, chloroform vapor annealing reverted the face-on-PII2T film to an edge-on orientation, while preserving a degree of anisotropic crystal alignment. Such a reversible crystal orientation transformation was driven by the difference in Gibbs free energy between the relatively thermodynamically stable edge-on state and the metastable face-on state. Characterization of various PII2T films revealed a definitive relationship between their charge transport properties and induced crystalline structures. Finally, this control strategy for switching crystal orientations can be readily applied to other conjugated polymers.