Core Level Shifts of Hydrogenated Pyridinic and Pyrrolic Nitrogen in the Nitrogen-Containing Graphene-Based Electrocatalysts: In-Plane vs Edge Defects

A combination of N 1s X-ray photoelectron spectroscopy (XPS) and first principles calculations of nitrogen-containing model electrocatalysts was used to elucidate the nature of the nitrogen defects that contribute to the binding energy (BE) range of the N 1s XPS spectra of these materials above ~400 eV. Experimental core level shifts were obtained for a set of model materials, namely N-doped carbon nanospheres, Fe–N–carbon nanospheres, polypyrrole, polypyridine, and pyridinium chloride, and were compared to the shifts calculated using density functional theory. The results confirm that the broad peak positioned at ~400.7 eV in the N 1s XPS spectra of N-containing catalysts, which is typically assigned to pyrrolic nitrogen, contains contributions from other hydrogenated nitrogen species such as hydrogenated pyridinic functionalities. Namely, N 1s BEs of hydrogenated pyridinic-N and pyrrolic-N were calculated as 400.6 and 400.7 eV, respectively, using the Perdew–Burke–Ernzerhof exchange-correlation functional. A special emphasis was placed on the study of the differences in the XPS imprint of N-containing defects that are situated in the plane and on the edges of the graphene sheet. Density functional theory calculations for BEs of the N 1s of in-plane and edge defects show that hydrogenated N defects are more sensitive to the change in the chemical environment in the carbon matrix than the non-hydrogenated N defects. In conclusion, calculations also show that edge-hydrogenated pyridinic-N and pyrrolic-N defects only contribute to the N 1s XPS peak located at ~400.7 eV if the graphene edges are oxygenated or terminated with bare carbon atoms.