The lattice fluid (LF) thermodynamic model and extended Vrentas' free-volume (E-VSD) theory were coupled to study the gas separation properties of the linear thermoplastic polyurethane (TPU) membranes with different chemical structures by analyzing their microstructures. A set of characteristic parameters were extracted using the repeating unit of the TPU samples and led to prediction of reliable polymer densities (AARD < 6%) and gas solubilities. The viscoelastic parameters, which were obtained from the DMTA analysis, were also estimated the gas diffusion vs. temperature, precisely. The degree of microphase mixing based on the DSC analysis was in order: TPU-1 (4.84 wt%) < TPU-2 (14.16 wt%) < TPU-3 (19.92 wt%). It was found that the TPU-1 membrane had the highest degree of crystallinity, but showed higher gas solubilities and permeabilities because this membrane has the least degree of microphase mixing. These values, in combination with the gas permeation results, showed that the content of the hard segment along with the degree of microphase mixing and other microstructural parameters like crystallinity were the determinative parameters.
Sadeghian et al. (Thu,) studied this question.