SiO2 aerogel cement composites (SACCs) are promising for building insulation, but how their residual thermal performance evolves after high-temperature exposure remains unclear, limiting fire protection assessment. In this study, SACC specimen with aerogel contents of 0%, 5%, 7%, and 10% were heat-treated at 400, 600, 700, 800, and 1000 °C. After cooling, their post-exposure thermal performance and microstructure were characterized via mass loss, density, thermal conductivity, MIP, and SEM. Results obtained at room temperature showed that with increasing treatment temperature, thermal conductivity first decreases and then increases, reaching a minimum after 700 °C treatment for the A7 specimens (from 0.092 to 0.063 W/(m·K)). Microstructural analysis of cooled specimens revealed that this non-monotonic behavior arises from three heat-induced changes: the cement matrix, aerogel aggregates, and the interfacial gap between them. After treatment at 700 °C, the gap corresponds to a Knudsen number of 0.01–0.02, entering the slip-flow regime. Combined with the low thermal conductivity of the cement matrix, this yields the best insulation. After treatment at 800 °C and above, the gap exceeded 60 μm, shifting heat transfer to the continuum regime and reducing insulation capacity. A thermal conductivity prediction model based on these post-exposure mechanisms agreed well with the experimental results.
Liu et al. (Fri,) studied this question.