Preparation and properties of chemical cellulose from ascidian tunic and their regenerated cellulose fibers

Chemical cellulose (dissolving pulp) was prepared from ascidian tunic by modified paper‐pulp process (prehydrolysis with acidic aqueous solution of H 2 SO 4 , digestion with alkali aqueous solution of NaOH/Na 2 S, bleaching with aqueous NaOCl solution, and washing with acetone/water). The α‐ cellulose content and the degree of polymerization (DPw) of the chemical cellulose was about 98 wt % and 918, respectively. The Japanese Industrial Standard (JIS) whiteness of the chemical cellulose was about 98%. From the X‐ray diffraction patterns and 13 C‐NMR spectrum, it was found that the chemical cellulose obtained here has cellulose Iβ crystal structure. A new regenerated cellulose fiber was prepared from the chemical cellulose by dry–wet spinning using N ‐methylmorpholine‐ N ‐oxide (NMMO)/water (87/13 wt %) as solvent. The new regenerated cellulose fiber prepared in this study has a higher ratio of wet‐to‐dry strength (<0.97) than commercially regenerated cellulose fibers.