Electron Microscopy of Dislocation Structures in SrTiO3 Deformed at High Temperatures

Dislocations in SrTiO3 deformed plastically by indentation at 900 and 1100 °C are studied by comprehensive transmission electron microscopy. At both 900 and 1100°C all the dislocations studied have Burgers vectors of either 〈100〉 or 〈110〉 type. At 900 °C both types of dislocation are in the glide configuration. On the other hand, at 1100°C 〈001〉 dislocations are in the climb configuration, although most of 〈110〉 dislocations are in the glide configuration. Small dislocation loops, both of 〈100〉 and 〈110〉 types, are observed, and most of them are identified as vacancy type. Mittels umfassender Transmissionselektronenmikroskopie werden in SrTiO3, das durch Eindruck bei 900 und 1100 °C plastisch verformt wird, Versetzungen untersucht. Sowohl bei 900 als auch bei 1100 CC haben alle untersuchten Versetzungen entweder Burgersvektoren vom 〈100〉- oder 〈110〉-Typ. Bei 900 °C sind beide Versetzungstypen in der Glehkonfiguration. Auf der anderen Seite sind die 〈001〉-Versetzungen bei 1100°C in der Kletterkonfiguration, obwohl die meisten der 〈110〉-Ver-setzungen in der Gleitkonfiguration sind. Kleine Versetzungsschleifen, sowohl vom 〈100〉-Typ als auch vom 〈110〉-Typ, werden beobachtet, und die meisten von ihnen als Leerstellentyp identi-fiziert.