Microtensile Bond Strength of a Resin Cement to Silica‐Based and Y‐TZP Ceramics Using Different Surface Treatments

PURPOSE: To evaluate the effects of different surface treatments on the microtensile bond strength (μTBS) of bonding between resin cement and lithia or zirconia-based ceramics using an in vitro study. MATERIALS AND METHODS: bonding areas. The specimens were thermocycled, and bond strength tests were performed in a universal testing machine. The fracture type was determined by observing the fractured surface under a stereomicroscope. The mean bond strengths of the specimens were statistically analyzed using one-way ANOVA and Duncan's tests (α = 0.05). RESULTS: Mean comparison of the μTBS showed no significant difference between LiSaE and LiSa (p > 0.05), but significant differences between LiSaE and other groups (p ≤ 0.01). No significant differences were found between the ZiSaLa and ZiSa groups (p > 0.05). The modes of failure in all groups were mostly adhesive (57% to 80%). The mean bond strengths in laser-irradiated ceramics were significantly lower than those from other surface treatments. All ZiLa specimens debonded before testing (pretest failure). CONCLUSIONS: Lithium disilicate ceramic surface treated with a combination of sandblasting and silane application provided a bond strength comparable to that provided by sandblasting in combination with acid etching and applying silane. Groups treated with laser irradiation had significantly lower bond strengths than other groups.