An n-type semiconducting diamond thin film was obtained by microwave enhanced plasma chemical vapor deposition using phosphine (PH3) as a dopant source. A homoepitaxial diamond thin film with a thickness of about 300 nm was grown on the 111 surface of a type Ib diamond with a variety of dopant concentrations. Over a wide range of dopant concentrations (PH3/CH4: 1000–20 000 ppm), the n-type conduction was confirmed by Hall-effect measurements. The activation energy of carriers was 0. 43 eV. The Hall mobility of about 23 cm2/V s has been obtained at around 500 K for the 1000 ppm sample. No significant increase of hydrogen has been observed by secondary-ion-mass-spectroscopy analysis for the phosphorous doped layers.